| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
90℃
|
Non-Immersed
160℃
|
||
| Product type | A glass fibre reinforced vinyl ester glass-flake lining. This product is a high performance vinylester lining containing both glassfibre and glassflake. | Recommended DFT | ||
| Description | As a rehabilitation and high performance lining for thinned/ corroded pipes and where additional tensile properties are required, Corrocoat Fibrecoat may be applied in single or multiple layers at up to 3000 microns per coat. | Greater than 3000 microns dependent upon duty and environment. This material is a barrier coating and the thickness needed is dependent upon service conditions and the existing condition of the substrate. |
||
| Surcface preparation | Metals: The surface must be decontaminated, degreased and loose materials removed from the surface. Where possible and for optimum performance, grit blast to ISO standard 8501-1 Sa 2½ or equivalent. | SDS | ||
Use applications
Coating method
＊There are more coating materials but we listed de most common use.
Water, sewerage, & wastewater
Corrocoat Corrofill VE
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
110℃
|
Non-Immersed
160℃
|
||
| Product type | A two-pack, vinyl ester filler and grouting material containing abrasionresistant fillers. | Recommended DFT | ||
| Description | As a pit filler or grout for badly pitted steel or other applications that require a high performance, chemically resistant coating system. | The material may be applied at DFT’s of up to 6mm but this thickness should not be exceeded in a single coat. | ||
| Surcface preparation | The surface to be coated should be free from grease etc. Metal should be grit blasted to a minimum ISO 8501-1 Sa 2½ near 3 or equivalent. All blast residues must be removed by sweeping or blowing clean and vacuuming where necessary. | SDS | ||
Corroglass AR4
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
82℃
|
Non-Immersed
ー
|
||
| Product type | Brominated interpenetrating polymer network system, enhanced with glass flake. | Recommended DFT | ||
| Description | Formulated to offer the best resistance to base environments i.e. sodium hydroxide/sodium hypochlorite. | 500 - 3000 Microns dependent upon service conditions | ||
| Surcface preparation | Metals: Grit blast to ISO standard 8501-1 Sa 2 near 3 standard or equivalent. (For full details refer to Corrocoat Surface Specification SP1). Concrete: Grit blast to remove surface laitance. See Corrocoat Surface Specification SP5. | SDS | ||
Corroglass 652
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
90℃
|
Non-Immersed
185℃
|
||
| Product type | Low build vinyl ester resin glass flake coating. | Recommended DFT | ||
| Description | Light duty immersion and arduous atmospheric conditions or as a surface veil for other grades. | 0.5 to 1.0mm in multiple coats. | ||
| Surcface preparation | Metals: Grit blast to ISO standard 8501-1 Sa 2 near 3 or equivalent. (For full details refer to Corrocoat Surface Preparation SP1.) Concrete: refer to Corrocoat SP5. | SDS | ||
Corroglass 632
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
110℃
|
Non-Immersed
185℃
|
||
| Product type | Medium viscosity glass flake coating based on top grade vinyl ester resin with low monomer content. | Recommended DFT | ||
| Description | Used for coating intricate components by brush, requiring ease of application and contour following i.e. pump impellers. Offers high chemical resistance. | 0.7 to 2.0mm in multiple coats. | ||
| Surcface preparation | The surface to be coated should be free from grease etc. Metal should be grit blasted to ISO 8501-1 Sa 2 near 3 or equivalent with a grit profile of at least 75 microns, 100-125 microns being the ideal key. | SDS | ||
Corroglass 602
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
110℃
|
Non-Immersed
185℃
|
||
| Product type | High build glass flake coating based on top grade vinyl ester resin with low monomer content. | Recommended DFT | ||
| Description | Build coat for 600 series specifications. Outstanding performance with good resistance to solvent attack. Ideal for demineralised or distilled water applications, as well as on metal and masonry. | 1.0 to 3.0mm in two coats. Or as advised, may be built up to any desired thickness for repair. | ||
| Surcface preparation | Metals: Grit blast to ISO standard 8501-1 Sa 2 near 3. Concrete: refer to Corrocoat SP5. | SDS | ||
POLYGLASS VE VEILCOAT
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
110℃
|
Non-Immersed
185℃
|
||
| Product type | A wax inhibited vinyl ester/acrylic surface veil coating. | Recommended DFT | ||
| Description | For use as a waxed surface veil to Polyglass materials where surface inhibition must be avoided. | 200-400 microns | ||
| Surcface preparation | Metals: Gritblast to ISO standard 8501-1 SA 2 near 3 or equivalent. (For full details refer to Corrocoat Surface Preparation SP1). | SDS | ||
POLYGLASS VEPG
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
110℃
|
Non-Immersed
175℃
|
||
| Product type | A two-pack cold cured vinyl ester/acrylic co-polymer enhanced with flaked glass, specifically formulated to be applied using pipe rolling rig. | Recommended DFT | ||
| Description | Immersed environments where superior resistance to chemical attack is required, VE is suitable for most chemical environments within the pH range of 0 to 13. | Between 750 and 3000 microns dependent upon environment. | ||
| Surcface preparation | Metals: Grit blast to ISO 8501-1 Sa 2½ near 3 or equivalent. For full details refer to Corrocoat Surface Specification SP1. Concrete: Grit blast to remove surface laitance. See Corrocoat Surface Specification SP5. | SDS | ||
POLYGLASS VEHA
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
110℃
|
Non-Immersed
185℃
|
||
| Product type | Vinyl ester acrylic co-polymer enhanced with glass flake for hand application. | Recommended DFT | ||
| Description | For small areas of application where spraying is impractical and for stripe coating spray grades of Polyglass. | When used alone two or more coats of Polyglass VEHAuntil a minimum DFT of 650 microns, over thickness is not detrimental. When used as a stripe coat a single layer of circa 300um, or as otherwise specified. |
||
| Surcface preparation | For optimum performance of these products under immersed conditions,grit blast steel to ISO standard 8501-1 Sa 2½ near 3 or equivalent, prior to application. For full details refer to Corrocoat Surface Preparation SP1 | SDS | ||
POLYGLASS VEF
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
110℃
|
Non-Immersed
185℃
|
||
| Product type | Vinyl ester/acrylic co-polymer loaded with glass flake and thixotroped with fibre. Spray application only. | Recommended DFT | ||
| Description | May be used in identical conditions to Polyglass VE, offering superior. corrosion, chemical and temperature resistance. |
500 to 3000 microns dependent upon service environment. | ||
| Surcface preparation | Metals: Grit blast to ISO standard 8501-1 Sa 2½ near 3 or equivalent. (For full details refer to Corrocoat Surface Preparation SP1.) Concrete: refer to Corrocoat SP5. | SDS | ||