| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
90℃
|
Non-Immersed
180℃
|
||
| Product type | A highly chemical resistant, high tensile strength, low viscosity vinyl/ester resin. | Recommended DFT | ||
| Description | For wetting over reinforcement materials such as glass fibre. | Dependent upon application and quantity of roving used. | ||
| Surcface preparation | Metal Surfaces: Grit blast to ISO 8501-1 Sa 2½ or near 3 standard or equivalent. For full details refer to Corrocoat Data Sheet SP1. The laminate will typically be applied over a primed surface. | SDS | ||
Use applications
Coating method
＊There are more coating materials but we listed de most common use.
CORROGLASS
Corroglass AR4
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
82℃
|
Non-Immersed
ー
|
||
| Product type | Brominated interpenetrating polymer network system, enhanced with glass flake. | Recommended DFT | ||
| Description | Formulated to offer the best resistance to base environments i.e. sodium hydroxide/sodium hypochlorite. | 500 - 3000 Microns dependent upon service conditions | ||
| Surcface preparation | Metals: Grit blast to ISO standard 8501-1 Sa 2 near 3 standard or equivalent. (For full details refer to Corrocoat Surface Specification SP1). Concrete: Grit blast to remove surface laitance. See Corrocoat Surface Specification SP5. | SDS | ||
Corroglass 652
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
90℃
|
Non-Immersed
185℃
|
||
| Product type | Low build vinyl ester resin glass flake coating. | Recommended DFT | ||
| Description | Light duty immersion and arduous atmospheric conditions or as a surface veil for other grades. | 0.5 to 1.0mm in multiple coats. | ||
| Surcface preparation | Metals: Grit blast to ISO standard 8501-1 Sa 2 near 3 or equivalent. (For full details refer to Corrocoat Surface Preparation SP1.) Concrete: refer to Corrocoat SP5. | SDS | ||
Corroglass 632
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
110℃
|
Non-Immersed
185℃
|
||
| Product type | Medium viscosity glass flake coating based on top grade vinyl ester resin with low monomer content. | Recommended DFT | ||
| Description | Used for coating intricate components by brush, requiring ease of application and contour following i.e. pump impellers. Offers high chemical resistance. | 0.7 to 2.0mm in multiple coats. | ||
| Surcface preparation | The surface to be coated should be free from grease etc. Metal should be grit blasted to ISO 8501-1 Sa 2 near 3 or equivalent with a grit profile of at least 75 microns, 100-125 microns being the ideal key. | SDS | ||
Corroglass 602
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
110℃
|
Non-Immersed
185℃
|
||
| Product type | High build glass flake coating based on top grade vinyl ester resin with low monomer content. | Recommended DFT | ||
| Description | Build coat for 600 series specifications. Outstanding performance with good resistance to solvent attack. Ideal for demineralised or distilled water applications, as well as on metal and masonry. | 1.0 to 3.0mm in two coats. Or as advised, may be built up to any desired thickness for repair. | ||
| Surcface preparation | Metals: Grit blast to ISO standard 8501-1 Sa 2 near 3. Concrete: refer to Corrocoat SP5. | SDS | ||
Corroglass 252
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
90℃
|
Non-Immersed
160℃
|
||
| Product type | Low build Bisphenol ‘A’ polyester coating. | Recommended DFT | ||
| Description | Light duty coating for atmospheric conditions or as a surface veil for heavy duty grades. | 0.5 to 1.0 mm in multiple coats | ||
| Surcface preparation | When used direct on to substrate, this should be on correctly prepared surfaces that should be free of contaminants and grit blasted to ISO Standard 8501-1 Sa 2½ or equivalent, with a surface profile of at least 50 microns. | SDS | ||
Corroglass 232
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
90℃
|
Non-Immersed
160℃
|
||
| Product type | Medium viscosity Bisphenol ‘A’ polyester glass flake. | Recommended DFT | ||
| Description | Used for coating intricate components by brush, requiring ease of application and contour following i.e. pump impellers. | 0.5 to 1.5 mm in multiple coats | ||
| Surcface preparation | The surface to be coated should be free from grease etc. Metal should be grit blasted to ISO Standard 8501-1 Sa 2½ or equivalent, with a surface profile of at least 75 microns, 100-125 microns being the ideal key. | SDS | ||
Corroglass 202
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
90℃
|
Non-Immersed
160℃
|
||
| Product type | High build glass flake coating based on Bisphenol ‘A’ polyester resin. | Recommended DFT | ||
| Description | Developed for applications where good corrosion, abrasion and chemical resistance is required. Ideal for small areas/components with either metal or masonry substrates in arduous conditions. | 1 to 3 mm in two coats or as advised, may be built up to any desired thickness for repair via multiple coats. | ||
| Surcface preparation | The surface to be coated should be free from grease etc. Metal should be grit blasted to ISO Standard 8501-1 Sa 2½ or equivalent, with a surface profile of at least 75 microns, 100-125 microns being the ideal key. | SDS | ||
Corroglass 200 Laminating Resin
| Product information | Coating method | Temperature limit | ||
|---|---|---|---|---|
| Application |
Immersed
90℃
|
Non-Immersed
160℃
|
||
| Product type | Pre-accelerated Bisphenol ‘A’ unsaturated ester low viscosity resin. | Recommended DFT | ||
| Description | For wetting over reinforcement materials such as glass fibre. May also be used for GRP constructions. | Not applicable | ||
| Surcface preparation | Metal Surfaces: Grit blast to ISO 8501-1 Sa 2½ or equivalent. For full details refer to Corrocoat Data Sheet SP1. | SDS | ||